Interfacial interactions in concretes with silica fume and SBR latex

ROSSIGNOLO, Joao Adriano
Fonte: ELSEVIER SCI LTD Publicador: ELSEVIER SCI LTD
Tipo: Artigo de Revista Científica
ENG
Relevância na Pesquisa
736.8118%
This paper deals with the effect of silica fume and styrene-butadiene latex (SBR) on the microstructure of the interfacial transition zone (ITZ) between Portland cement paste and aggregates (basalt). Scanning electron microscope (SEM) equipped with energy dispersive X-ray analysis system (EDX) was used to determine the ITZ thickness. In the plain concrete a marked ITZ around the aggregate particles (55 mu m) was observed, while in concretes with silica fume or latex SBR the ITZ was less pronounced (35-40 mu m). However, better results were observed in concretes with silica fume and latex SBR (20-25 mu m). (C) 2008 Elsevier Ltd. All rights reserved.; Research Sponsoring Foundation of Sao Paulo State (Fundacao de Apoio a Pesquisa do Estado de Sao Paulo - FAPESP); Civil Engineering National Laboratory (Laboratorio Nacional de Engenharia Civil - LNEC) in Lisbon, Portugal

"Estudo de concretos de alto desempenho frente à ação de cloretos" ; Study of high performance concrete subjected to chloride attack

Silva, Fernanda Giannotti da
Fonte: Biblioteca Digitais de Teses e Dissertações da USP Publicador: Biblioteca Digitais de Teses e Dissertações da USP
Tipo: Tese de Doutorado Formato: application/pdf
Publicado em 25/05/2006 PT
Relevância na Pesquisa
533.8416%
Atualmente, um dos principais problemas ligados às estruturas de concreto armado é a corrosão da armadura, especialmente devido à ação dos íons cloreto. Sua incidência no contexto das principais manifestações patológicas encontradas nas construções é bastante significativa, chegando a atingir índices de 50% em algumas regiões brasileiras. Além disso, o custo do reparo ou da reabilitação das estruturas deterioradas, em alguns casos, pode ser superior ao de uma estrutura nova. Com o objetivo de aumentar a vida útil das estruturas de concreto e diminuir o índice de ocorrência da corrosão de armaduras, esta pesquisa verifica o comportamento de concretos com adições minerais quanto à eficiência na proteção do aço contra a corrosão induzida por íons cloreto, em relação ao concreto sem adição. Para a produção dos concretos de alto desempenho (CAD), foram utilizados dois tipos de adições: a sílica de Fe-Si ou silício metálico (SFS), já comercialmente disponível, e a sílica extraída da casca de arroz (SCA), produzida em laboratório. Assim, além de proporcionar uma barreira física à entrada de agentes agressivos na camada de cobrimento, a utilização desses concretos contribui para a diminuição da poluição ambiental...

Efeito de adições ativas na mitigação das reações álcali-sílica e álcali-silicato.; Effect of mineral admixtures in controlling the alkali-silica reaction and alkali-silicate reaction.

Munhoz, Flávio André da Cunha
Fonte: Biblioteca Digitais de Teses e Dissertações da USP Publicador: Biblioteca Digitais de Teses e Dissertações da USP
Tipo: Dissertação de Mestrado Formato: application/pdf
Publicado em 03/08/2007 PT
Relevância na Pesquisa
632.5378%
A reação álcali-agregado é uma manifestação patológica diretamente ligada à seleção dos materiais (cimento, agregados miúdo e graúdo, água e aditivos) que pode comprometer a durabilidade das estruturas de concreto, uma vez que a interação desses materiais e as condições ambientais é que vão conferir ao concreto determinadas propriedades ligadas à sua vida útil. A reação entre os hidróxidos alcalinos solubilizados na fase líquida dos poros dos concretos e alguns agregados reativos é lenta e resulta em um gel que, ao se acumular em vazios do concreto e na interface pasta-agregado, na presença de água, se expande, exercendo pressão interna no concreto. Ao exceder a resistência à tração do concreto, a pressão interna pode promover fissurações. A reação álcali-agregado requer a atuação conjunta de água, agregado reativo e álcalis. Sua prevenção pode ser feita a partir da eliminação de um dos fatores, ou seja, a partir do emprego de agregados inertes ou de cimentos com baixos teores de álcalis ou isolamento da umidade. Na impossibilidade de eliminar um dos fatores, medidas preventivas devem ser tomadas para o emprego de agregados reativos em obras de construção civil. Entre essas, destacam-se a utilização de cimentos com baixos teores de álcalis ou a de cimentos com adições ativas mitigadoras da reação álcali-agregado: escória de alto-forno...

Estudo da influência das adições de sílica ativa e copolímero estireno acrílico nas propriedades de argamassas para assentamento de porcelanato; Study of the copolymer styrene acrylic and silica fume adittions influence in the properties of mortars to fix porcelain stoneware tiles

Almeida, Alessandra Etuko Feuzicana de Souza
Fonte: Biblioteca Digitais de Teses e Dissertações da USP Publicador: Biblioteca Digitais de Teses e Dissertações da USP
Tipo: Tese de Doutorado Formato: application/pdf
Publicado em 16/09/2005 PT
Relevância na Pesquisa
737.28016%
Apesar de suas excelentes características técnicas e estéticas, a aplicação de porcelanato em fachadas requer especial atenção devido ser um material diferente das cerâmicas convencionais, além de que as fachadas estão sujeitas a diversos agentes capazes de danificar os revestimentos cerâmicos. O baixo índice de absorção de água do porcelanato é a principal causa da perda ou falta de aderência entre o tardoz e a argamassa colante, pois não permite o mecanismo de aderência mecânica existente nas cerâmicas porosas. O presente trabalho visa o estudo de argamassas com adições de látex base estireno acrílico e sílica ativa para o assentamento de porcelanato em fachadas a fim de evitar o aparecimento de patologias decorrentes da falta de aderência. Foram realizados ensaios normalizados para a avaliação das propriedades das argamassas quanto à fixação do porcelanato, além de procedimentos experimentais para a avaliação da microestrutura tais como análises térmicas, difração de raios-X, porosimetria por intrusão de mercúrio, espectroscopia de infravermelho e microscopia eletrônica de varredura associada à espectrografia por dispersão de energia. Os resultados obtidos mostraram que a adição combinada de polímero e sílica ativa às argamassas resultou em elevadas propriedades mecânicas e alta resistência de aderência...

Contribuição ao estudo da carbonatação do concreto com adição de sílica ativa em ambiente natural e acelerado

Possan, Edna
Fonte: Universidade Federal do Rio Grande do Sul Publicador: Universidade Federal do Rio Grande do Sul
Tipo: Dissertação Formato: application/pdf
POR
Relevância na Pesquisa
642.65297%
Devido à preocupação com a durabilidade das estruturas de concreto armado surgiram novas linhas de pesquisa destacando-se, dentre elas, a previsão de vida útil. Estes estudos deram origem a diversos modelos que tentam estabelecer o comportamento do concreto quando exposto a ambientes agressivos durante um determinado período. Existem várias maneiras de se modelar este comportamento: com base em resultados obtidos em experiências anteriores; a partir de ensaios de degradação acelerados; por métodos determinísticos e probabilísticos ou estocásticos. A estimativa de vida útil das estruturas de concreto empregando dados de ensaios acelerados é recomendada pela ASTM E-632 (1996) desde que estes sejam correlacionados com resultados de ensaios não acelerados ou naturais. A correlação entre estes ensaios possibilita a determinação dos coeficientes de aceleração, os quais expressam o número de vezes em que o ensaio acelerado representa o fenômeno de degradação natural. Dentro deste contexto o presente trabalho avalia a carbonatação do concreto com e sem adição de sílica ativa exposto a degradação natural e acelerada, verificando também a influência do teor desta adição e da relação água/aglomerante na carbonatação. Em paralelo foram determinados os coeficientes de carbonatação (kc) e de aceleração (αa). Os concretos estudados possuem relação água/aglomerante de 0...

Avaliação preliminar do resíduo caulinítico das indústrias de beneficiamento de caulim como matéria-prima na produção de uma metacaulinita altamente reativa

Barata, Marcio Santos; Dal Molin, Denise Carpena Coitinho
Fonte: Universidade Federal do Rio Grande do Sul Publicador: Universidade Federal do Rio Grande do Sul
Tipo: Artigo de Revista Científica Formato: application/pdf
POR
Relevância na Pesquisa
541.94285%
Este trabalho avaliou as potencialidades de emprego do resíduo caulinítico das indústrias de beneficiamento do caulim como matériaprima na produção de uma metacaulinita altamente reativa. As características mineralógicas do resíduo e da metacaulinita foram analisadas pela difratometria de raios X e pela análise térmica diferencial. A atividade pozolânica da metacaulinita foi determinada em argamassas de cimento Portland. O efeito da incorporação da metacaulinita no concreto foi investigado pela resistência à compressão e por um teste de absorção capilar de água. O percentual de adição adotado foi de 10% e as relações água/aglomerante escolhidas foram 0,39, 0,47 e 0,65. Além das misturas de referência, foram também moldados concretos com sílica ativa. O índice de atividade pozolânica da metacaulinita foi de 103%, semelhante ao da sílica ativa. Os concretos com metacaulinita apresentaram resistências à compressão superiores aos de referência e similares aos com sílica ativa. Quanto à absorção capilar, os concretos com metacaulinita apresentaram taxas de absorção de água entre 0,73 e 0,98 mm/h1/2, similares às dos concretos com sílica ativa e significativamente inferiores às dos concretos de referência. Os resultados demonstram que este resíduo caulinítico é uma excelente matéria-prima para fabricação de metacaulinita de alta reatividade.; This work has assessed potential uses of kaolinitic waste from kaolin processing industries as a raw material for the production of a highly reactive metakaolinite. The mineralogical characteristics of both this residue and also of the metakaolinite have been determined by X-ray diffraction and by differential thermal analysis. The metakaolinite pozzolanic activity was measured using Portland cement mortars. Resulting effects derived from metakaolinite incorporation on concrete were evaluated through compressive strength and water absorption tests. A 10% value was adopted for this incorporation procedure...

Avaliação das propriedades fisicas e mecanicas de concretos produzidos com os cimentos Portland de alta resistencia inicial e de alto-forno aditivados com silica ativa curados termicamente; Evaluation of physical and mechanical properties of steam cured concrete made with high early strenght Portland cement and blastfurnace slag cement containing silica fume

Paulo Sergio Bardella
Fonte: Biblioteca Digital da Unicamp Publicador: Biblioteca Digital da Unicamp
Tipo: Dissertação de Mestrado Formato: application/pdf
Publicado em 19/01/2005 PT
Relevância na Pesquisa
736.20484%
A durabilidade das estruturas de concreto depende da estrutura porosa e da impermeabilidade do concreto, uma vez que a entrada de água e de agentes deletérios iniciam os processos patológicos que diminuem a vida útil de uma estrutura de concreto. Dessa forma, o objetivo deste trabalho foi avaliar a resistência mecânica, permeabilidade, absorção e carbonatação natural de concretos submetidos a diferentes condições de cura. Os procedimentos de cura adotados são normalmente utilizadds em canteiros de obra e na produção de estruturas pré-moldadas de concreto: cura imersa até a idade de 7 dias, cura ambiente e cura térmica. A cura térmica foi realizada na temperatura de 60°C. Foram empregados concretos produzidos com cimento Portland de Alta Resistência Inicial (CP V ARI) e cimento Portland de Alto Forno (CP III) sem e com sílica ativa (em substituição ao cimento na proporção de 10% em massa) para cada um dos diferentes tipos de cura utilizados. Os resultados evidenciaram que o tipo de cura afeta o desempenho do concreto. A mudança do tipo de cura aplicada proporcionou variações nas propriedades mecânicas e na durabilidade dos concretos, principalmente no que diz respeito à sua estrutura porosa. Assim, um regime de cura adequado é essencial para garantir a resistência mecânica e a durabilidade dos concretos. A utilização de sílica ativa em substituição ao cimento melhorou o desempenho dos concretos...

Avaliação do desempenho de aglomerante a base de gesso com cimento portland de alto forno e silica ativa; Perfomance assessment of gypsum cement based rendering materials containing portland blast-furnce slag cement and condensed silica fume

Jose Antonio De Milito
Fonte: Biblioteca Digital da Unicamp Publicador: Biblioteca Digital da Unicamp
Tipo: Tese de Doutorado Formato: application/pdf
Publicado em 07/02/2007 PT
Relevância na Pesquisa
738.1447%
O gesso é um aglomerante que tem sido muito empregado em revestimento de paredes. Apresenta um bom desempenho, é econômico e de fácil aplicação, mas limitado ao uso interno devido a sua sensibilidade à água. Algumas tentativas têm sido realizadas para melhorar a sua utilização em ambientes sujeitos à umidade. Neste sentido, pesquisas avançam na tentativa de empregar diferentes adições como resinas epóxi, polímeros, cimentos, escórias, impermeabilizantes, entre outros. O objetivo desta tese foi avaliar o desempenho das misturas de gesso com cimento Portland de Alto Forno e sílica ativa nos revestimentos internos e externos sujeitos à umidade. Para isso verificaram-se as propriedades macroscópicas das misturas por meio de ensaios físicos, químicos, físico-químicos e também a avaliação microestrutural utilizando a microscopia eletrônica de varredura. As misturas foram aplicadas em revestimentos de painéis de alvenaria de blocos de concreto e observados visualmente por um período de cinco anos. Além da observação visual foi verificada a resistência de aderência das misturas aplicadas internamente e externamente. Dos resultados obtidos observou-se uma possível coexistência entre o gesso e o cimento e que a adição de sílica ativa na mistura reduz a formação de etringita...

Thermogravimetric analyses and mineralogical study of polymer modified mortar with silica fume

Almeida,Alessandra Etuko Feuzicana de Souza; Sichieri,Eduvaldo Paulo
Fonte: ABM, ABC, ABPol Publicador: ABM, ABC, ABPol
Tipo: Artigo de Revista Científica Formato: text/html
Publicado em 01/09/2006 EN
Relevância na Pesquisa
736.8118%
Mineral and organic additions are often used in mortars to improve their properties. Microstructural investigation concerning the effects of styrene acrylic polymer and silica fume on the mineralogical composition of high-early-strength portland cement pastes after 28 days of hydration are presented in this paper. Thermogravimetry and derivative thermogravimetry were used to study the interaction between polymers and cement, as well as the extent of pozzolanic reaction of the mortars with silica fume. Differential scanning calorimetry and X ray diffraction were used to investigate the cement hydration and the effect of the additions. The results showed that the addition of silica fume and polymer reduces the portlandite formation due to delaying of Portland cement hydration and pozzolanic reaction.

Effect of silica fume and SBR latex on the pasteaggregate interfacial transition zone

Rossignolo,João Adriano
Fonte: ABM, ABC, ABPol Publicador: ABM, ABC, ABPol
Tipo: Artigo de Revista Científica Formato: text/html
Publicado em 01/03/2007 EN
Relevância na Pesquisa
736.8118%
This paper deals with the effect of silica fume and styrene-butadiene latex (SBR) on the microstructure of the interfacial transition zone (ITZ) between Portland cement paste and aggregates (basalt). Scanning Electron Microscope (SEM) equipped with energy dispersive x ray analysis system (EDX) was used to determine the ITZ thickness. In the plain concrete a marked ITZ around the aggregate particles (55 µm) was observed, while in concretes with silica fume or latex SBR the ITZ was less pronounced (35-40 µm). However, better results were observed in concretes with silica fume and latex SBR (20-25 µm).

Comparative study of the characteristics of nano silica - , silica fume - and fly ash - incorporated cement mortars

Biricik,Hasan; Sarier,Nihal
Fonte: ABM, ABC, ABPol Publicador: ABM, ABC, ABPol
Tipo: Artigo de Revista Científica Formato: text/html
Publicado em 01/06/2014 EN
Relevância na Pesquisa
729.224%
The structural characteristics of cement mortars, impregnated with nano silica (NS), silica fume (SF) and fly ash (FA), were comparatively studied using Fourier transform infrared spectrometer (FTIR), thermogravimeter-differential thermogravimeter (TG-DTG) and scanning electron microscope (SEM). The mechanical strengths of the specimens were determined at early (7th day) and standard (28th day) curing ages. The compressive strengths and flexural strengths developed in the mortar specimens containing NS particles were found considerably higher than those of the corresponding specimens of SF and FA over and above the control at both ages. FTIR, TG-DTG and SEM analyses results were consistent with the remarkable increase in the mechanical strength of the mortars with NS. These increases in the strengths of the mortars with NS are attributable to the nano sized particles and extensive surface area of NS. The nano sized particles, as nucleating agents, promoted the hydration of C3S and C2S and the formation of C - S - H phase. Plenty of active sites on the surface of NS particles induced their pozzolanic reactivity and the extent of bond formation between NS particles and free CH.

Chloride accelerated test: influence of silica fume, water/binder ratio and concrete cover thickness

Pereira,E.; Resende,A.; Medeiros,M. H. F. de; Meneghetti,L. C.
Fonte: IBRACON - Instituto Brasileiro do Concreto Publicador: IBRACON - Instituto Brasileiro do Concreto
Tipo: Artigo de Revista Científica Formato: text/html
Publicado em 01/08/2013 EN
Relevância na Pesquisa
730.4974%
In developed countries like the UK, France, Italy and Germany, it is estimated that spending on maintenance and repair is practically the same as investment in new constructions. Therefore, this paper aims to study different ways of interfering in the corrosion kinetic using an accelerated corrosion test - CAIM, that simulates the chloride attack. The three variables are: concrete cover thickness, use of silica fume and the water/binder ratio. It was found, by analysis of variance of the weight loss of the steel bars and chloride content in the concrete cover thickness, there is significant influence of the three variables. Also, the results indicate that the addition of silica fume is the path to improve the corrosion protection of low water/binder ratio concretes (like 0.4) and elevation of the concrete cover thickness is the most effective solution to increase protection of high water/binder ratio concrete (above 0.5).

Development of UHPC Mixtures Utilizing Natural and Industrial Waste Materials as Partial Replacements of Silica Fume and Sand

Ahmad, Shamsad; Hakeem, Ibrahim; Maslehuddin, Mohammed
Fonte: Hindawi Publishing Corporation Publicador: Hindawi Publishing Corporation
Tipo: Artigo de Revista Científica
EN
Relevância na Pesquisa
530.49742%
In the exploratory study presented in this paper, an attempt was made to develop different mixtures of ultrahigh performance concrete (UHPC) using various locally available natural and industrial waste materials as partial replacements of silica fume and sand. Materials such as natural pozzolana (NP), fly ash (FA), limestone powder (LSP), cement kiln dust (CKD), and pulverized steel slag (PSS), all of which are abundantly available in Saudi Arabia at little or no cost, were employed in the development of the UHPC mixtures. A base mixture of UHPC without replacement of silica fume or sand was selected and a total of 24 trial mixtures of UHPC were prepared using different percentages of NP, FA, LSP, CKD, and PSS, partially replacing the silica fume and sand. Flow and 28-d compressive strength of each UHPC mixture were determined to finally select those mixtures, which satisfied the minimum flow and strength criteria of UHPC. The test results showed that the utilization of NP, FA, LSP, CKD, and PSS in production of UHPC is possible with acceptable flow and strength. A total of 10 UHPC mixtures were identified with flow and strength equal to or more than the minimum required.

Desempenho de argamassas com sílica ativa em ambiente marinho.; Performance od sílica fume mortsrs in marine environment.

Almeida, David Costa de
Fonte: Universidade Federal de Alagoas; BR; Estruturas; Programa de Pós-Graduação em Engenharia Civil; UFAL Publicador: Universidade Federal de Alagoas; BR; Estruturas; Programa de Pós-Graduação em Engenharia Civil; UFAL
Tipo: Dissertação Formato: application/pdf
POR
Relevância na Pesquisa
747.63164%
The repair of reinforced concrete structures attracts more and more attention of researchers and constructors who see an ever growing number of pathologic phenomenons on several constructions that make use of this widely accepted material. The wrong notion which claims the concrete is an eternal and unchangeable matter has been definitively substituted by the fact that it s a dynamic and complex substance, vulnerable to several aggressive compounds which modify and cause damage to its chemical and physical structure. The present work intended to gather data about the performance of silica fume as a chemical admixture to mortars under the marine atmosphere in the tidal zone, and also evaluate if the magnesium sulfate has any major role in the development of the mortar s properties. To achieve the objectives of the study two groups of mortar were made, one used silica in its composition, and the other didn t. The mortar was cast in cylindrical and prismatic molds to, later, be subjected to natural drying and wetting cycles in the sea coast of Maceió. The cylindrical specimens were 10 x 5 cm and the prismatic ones were 50 x 15 x 4 cm and had reinforcement inside. The tests were conducted in the ages of 14, 28, 91, 135 and 180 days and concerned measuring the compressive...

Contribuição aos estudos da influência da nanossílica nas propriedades mecânicas e na trabalhabilidade de concretos para produção em centrais e para fabricação de pré-moldados; Contribution to the studies of the influence of nanosilica on the mechanical properties and workability of concretes for batching plants and for manufacture of precast pieces

Moraes, Mayara Queiroz
Fonte: Universidade Federal de Goiás; Brasil; UFG; Programa de Pós-graduação em Engenharia Civil (EEC); Escola de Engenharia Civil - EEC (RG) Publicador: Universidade Federal de Goiás; Brasil; UFG; Programa de Pós-graduação em Engenharia Civil (EEC); Escola de Engenharia Civil - EEC (RG)
Tipo: Dissertação Formato: application/pdf
POR
Relevância na Pesquisa
542.65297%
Unlike the silica fume, whose benefits on the properties of the concretes are already widely known, little is known regarding nanosilica. This research offers an analysis of the contribution of different types of nanosilica in mechanical characteristics and workability maintenance of concretes, as well as an evaluation of the behavior of these additions when subjected to steam curing. For this, there were compared among themselves laboratory test results in concretes with different characteristics and different purposes (one of them suitable for production at batching plants and the other for metering precast elements). The results confirmed advantages for the simple addition of nanossílica at mechanical properties of concretes for batching plants with strengths above 40 MPa (a/c<0.52), but showed that the most advantageous situation consists in adding it together with sílica fume, since the concrete with both additions exceeded the reference concrete above 36 MPa (a/c<0.615), which highlights the importance of combining pozzolanic effect of silica fume, the creation of nucleation sites caused by nanossílica and better packaging mix, size distribution generated by the two additions give the folder.Regarding the maintenance of workability...

Influence of silica fume on stress-strain behavior of FRP-confined HSC

Lim, J.; Ozbakkaloglu, T.
Fonte: Swinburne University of Technology; online Publicador: Swinburne University of Technology; online
Tipo: Conference paper
Publicado em //2013 EN
Relevância na Pesquisa
747.5188%
Confinement of high-strength concrete (HSC) columns with fiber reinforced polymer (FRP) composites has been receiving increasing research attention due to the advantageous engineering properties offered by the composite system. The use of silica fume as a concrete additive is a widely accepted practice in producing HSC. However, the influence of presence and amount of silica fume on the efficiency of FRP confinement has not been clearly understood. This paper presents results of an experimental study on the influence of silica fume on FRP-confined HSC. Nine aramid FRP (AFRP)-confined and nine unconfined concrete cylinders were tested under axial compression. The change in the mechanical properties of FRP-confined and unconfined HSC with silica fume amount was investigated. The results indicate that the compressive strength of unconfined concrete increases with an increase in the amount of silica fume. However, this increase comes at a cost of increased concrete brittleness, which adversely affects the effectiveness of FRP confinement. These observations were further validated with 93 test results of FRP-confined HSC assembled from the published literature. The additional results from the database allowed further observations to be made on the influence of silica fume on the compressive behavior of FRP-confined HSC. This paper presents the findings of these investigations.; J. C. Lim...

Fabricação de tijolos modulares de solo-cimento por prensagem manual com e sem adição de sílica ativa; Production of soil-cement modular bricks by manual pressing with and without silica fume addition

Grande, Fernando Mazzeo
Fonte: Biblioteca Digitais de Teses e Dissertações da USP Publicador: Biblioteca Digitais de Teses e Dissertações da USP
Tipo: Dissertação de Mestrado Formato: application/pdf
Publicado em 10/02/2003 PT
Relevância na Pesquisa
620.11285%
Neste trabalho, por meio de uma metodologia experimental foram analisados vários aspectos de tijolos modulares compostos por misturas binárias e ternárias de solo-cimento e solo cimento-sílica produzidos em prensa manual modelo SAHARA, com a finalidade de se obter parâmetros e diretrizes que visam um melhor desempenho do material. Realizaram-se ensaios em corpos-de-prova cilíndricos de maneira acessória no decorrer do trabalho, o que resultou no suporte para fundamentação de diversas avaliações sobre as composições de traços utilizados na fabricação dos tijolos. Foram executados painéis de parede com o objetivo de verificar o comportamento da alvenaria em relação à resistência à compressão e à deformabilidade das paredes, possibilitando correlações com os resultados dos ensaios de prismas, tijolos e argamassa de assentamento. As contribuições da pesquisa permitem relacionar a tecnologia da fabricação de tijolos de solo-cimento com o contexto de construção sustentável e o aproveitamento de resíduos industriais, além de sistematizar informações para a elaboração de um projeto tecnológico com os tijolos modulares; In this work, several aspects of modular bricks composed by binary and ternary mixtures of soil-cement and soil-cement-silica...

Sulphatic characterization of rice husk ashes. Comparative study with the Spanish silica fume

Talero Morales, Rafael; Pedrajas, C.; Delgado, A.; Rahhal, V.
Fonte: Conselho Superior de Investigações Científicas Publicador: Conselho Superior de Investigações Científicas
Tipo: Comunicación de congreso Formato: 154573 bytes; application/pdf
ENG
Relevância na Pesquisa
724.89055%
En: 1st Spanish National Conference on Advances in Materials Recycling and Eco – Energy Madrid, 12-13 November 2009.-- Editors: F. A. López, F. Puertas, F. J. Alguacil and A. Guerrero.-- 4 pages, 3 tables.; In this investigation it has determinated the "chemical character" by sulphatic characterization of two industrial incinerated residues, ashes C1 and C2, in order to incorporate them as puzzolanic addition, in the manufacture of cements, traditional or high resistance concretes and mortars. Also, It was considered carry out a comparative study with the Spanish silica fume, HS. Then, experimental results showed that the two ashes, can be considerate as artificial puzzolanic additions with silicic "chemical character", but only one of them that of major content of SiO2, C2, could become considerate as “microsilica On the other hand, C1 couldn´t be considerated, because the content of P.F. resulted too high, although the content of reactive silica, SiO2r- was bigger than de content of C2. For this motive, the C1 ash was refused for this propose, in spite of in the sulphatic characterization it showed a more near conduct to HS.; Peer reviewed

HYDRAULIC CONDUCTIVITY OF GCL WITH BENTONITE – SILICA FUME MATRIX (doi: 10.4090/juee.2012.v6n2.109112)

Andal, Mudimby; Chandrasekhar, M.; Viswanadh, G. K.
Fonte: JUEE Press Publicador: JUEE Press
Tipo: info:eu-repo/semantics/article; info:eu-repo/semantics/publishedVersion; Formato: application/pdf
Publicado em 26/12/2012 ENG
Relevância na Pesquisa
541.3722%
This paper presents the influence of partial replacement of bentonite by silica fume which is used in the manufacture of Geosynthetic Clay Liner (GCL). Geosynthetic Clay Liners consist bentonite (Sodium Based) sandwiched between two geotextile. Benotinite, having low permeability imparts better hydraulic performance to the GCL to act as liner. In this investigation, an attempt has been made to study the hydraulic conductivity of GCL with modified Bentonite. The bentonite is partially replaced by silica fume, a waste product of ferroalloy industries. Silica fume reduces the cracking characteristics of bentonite on desiccation. The replacement levels varied from 0% to 50% at a gradual increment of 5%. The test results indicated that partial replacement of bentonite by silica fume did not affected the permeability of bentonite even at 30%. Beyond 45% replacement levels the bentonite- silica fume mixtures showed increased permeability. This increased permeability also well within permeability limits of liners 1×10-9 m/sec.

EFFECT OF SILICA FUME ADDITION ON THE CHLORIDE-RELATED TRANSPORT PROPERTIES OF HIGH-PERFORMANCE CONCRETE

LIZARAZO-MARRIAGA,JUAN; LÓPEZ YÉPEZ,LUCIO GUILLERMO
Fonte: DYNA Publicador: DYNA
Tipo: Artigo de Revista Científica Formato: text/html
Publicado em 01/02/2012 EN
Relevância na Pesquisa
730.4974%
Being the corrosion of steel reinforcement due to chloride penetration the major cause of durability problems in concrete, this paper summarizes the results of an experimental research carried out in order to investigate the influence of the silica fume (SF) content on some chloride-related transport properties. To achieve this, the compressive strength, the self-diffusion chloride penetration, the charge passed in a non-steady chloride migration test (ASTM C1202), and the AC resistivity were measured on concrete mixes of high-performance concrete. Four concrete mixes were cast incorporating 5, 10, and 15% of SF as an addition to ordinary Portland cement. The results showed that the silica fume in concrete causes an increase in strength and a reduction in chloride ion permeability; however, clear differences were found between the results of long diffusion and rapid electrical tests.