PREPARAÇÃO DE COMPÓSITOS DE POLIANILINA EM MATRIZES DE COPOLÍMEROS ESTIRENO-DIVINILBENZENO E ESTUDOS DE ADSORÇÃO POR TROCA IÔNICA DE ÂNIONS COMPLEXOS DE [FeCl4]- E [CuCl4]2-; PREPARATION FOR SUPPORTING COMPOSITE POLIANYLINE IN MATRIZES OF COPOLYMERS ESTYRENE-DIVINYLBENZENE AND STUDIES OF ADSORPTION BY EXCHANGE IONIC OF COMPLEX ANIONS OF [FeCl4]- AND [CuCl4] 2-

SILVA, Robson Benedito
Fonte: Universidade Federal de Goiás; BR; UFG; Mestrado em Química; Educação em Química Publicador: Universidade Federal de Goiás; BR; UFG; Mestrado em Química; Educação em Química
Tipo: Dissertação Formato: application/pdf
POR
Relevância na Pesquisa
303.95977%
In this work, composites of dispersed polyaniline in beads of styrenedivinybenzene copolymer (Pani/Sty-DVB copopolymer) with different porosities were prepared through in situ polymerization. Materials with high surface areas and high porosities were obtained what explain their properties to adsorve transition metals. SD29 and SD84 copolymers were prepared through suspension polymerization in the presence of inert diluents as toluene/heptane with different DVB ratios to obtain macroporous beads. SD29/Pani and SD84/Pani composites were obtained by swelling the copolymers with aniline/ethanol mixtures (20/80%) before polymerization. Oxidative polymerization of aniline was carried out with ammonium persulfate in the presence of nitric acid at pH extremely acid and temperature range from 0 to 3 oC for 5 hours. All materials were characterized by infrared spectroscopy, porosity measurements, optical microscopy and adsorption capacity. The composite surface areas and pore volumes diminished in relation to original xv copolymers, while apparent density increased due polyaniline incorporation. Pore size distributions did not suffer large variations and all were typical of macroporous structures. Due the high DVB content, SD84/Pani composite and SD84 copolymer presented higher porosity and specific surface area when compared to systems with low reticulation degree. From acid solutions...