Página 1 dos resultados de 69 itens digitais encontrados em 0.115 segundos

Microtensile bond strength of composite resin to glass-infiltrated alumina composite conditioned with Er,Cr:YSGG laser

Eduardo, Carlos de Paula; Silva, Marina Stella Bello; Moretto, Simone Gonçalves; Cesar, Paulo Francisco; Silva, Patricia Moreira de Freitas Costa e
Fonte: SPRINGER LONDON LTD; LONDON Publicador: SPRINGER LONDON LTD; LONDON
Tipo: Artigo de Revista Científica
ENG
Relevância na Pesquisa
56.14%
Tribochemical silica-coating is the recommended conditioning method for improving glass-infiltrated alumina composite adhesion to resin cement. High-intensity lasers have been considered as an alternative for this purpose. This study evaluated the morphological effects of Er,Cr:YSGG laser irradiation on aluminous ceramic, and verified the microtensile bond strength of composite resin to ceramic following silica coating or laser irradiation. In-Ceram Alumina ceramic blocks were polished, submitted to airborne particle abrasion (110 mu m Al(2)O(3)), and conditioned with: (CG) tribochemical silica coating (110 mu m SiO(2)) + silanization (control group); (L1-L10) Er,Cr:YSGG laser (2.78 mu m, 20 Hz, 0.5 to 5.0 W) + silanization. Composite resin blocks were cemented to the ceramic blocks with resin cement. These sets were stored in 37A degrees C distilled water (24 h), embedded in acrylic resin, and sectioned to produce bar specimens that were submitted to microtensile testing. Bond strength values (MPa) were statistically analyzed (alpha a parts per thousand currency sign0.05), and failure modes were determined. Additional ceramic blocks were conditioned for qualitative analysis of the topography under SEM. There were no significant differences among silicatization and laser treatments (p > 0.05). Microtensile bond strength ranged from 19.2 to 27.9 MPa...

Influência da técnica de microinfiltração, pressão pulpar simulada, armazenamento e fadiga cíclica na microinfiltração e integridade marginal das coroas In-Ceram Alumina; Influence of microleakage technique, simulated pulpal pressure, water storage, and cyclic fatigue on marginal integrity and microleakage of In-Ceram alumina crowns

Rossetti, Paulo Henrique Orlato
Fonte: Biblioteca Digitais de Teses e Dissertações da USP Publicador: Biblioteca Digitais de Teses e Dissertações da USP
Tipo: Tese de Doutorado Formato: application/pdf
Publicado em 06/06/2007 PT
Relevância na Pesquisa
66.57%
Objetivos: verificar a influência da técnica de microinfiltração, pressão pulpar simulada, armazenamento e fadiga cíclica na microinfiltração e integridade marginal das coroas In-Ceram alumina. Material e métodos: Dentes pré-molares superiores humanos de dimensões semelhantes receberam preparos para coroa total com 4mm de altura, 6 graus de convergência e 2mm de desgaste axial e oclusal. Coroas de In-Ceram alumina com 0,5mm de espessura foram obtidas e cimentadas com Panavia F/Clearfil SE Bond (PAN-SE) e/ou Rely XARC/Adper Single Bond 2 (REL-SB). Quatro hipóteses foram testadas: 1) Ausência de diferença na microinfiltração entre uma nova técnica sugerida para verificar a microinfiltração, quando comparada à técnica convencional, 1.1) Verificar se a nova técnica é adequada para estudos laboratoriais de microinfiltração, 2) A pressão pulpar simulada (15cmH2O) não altera a microinfiltração; 3) O armazenamento (90 dias) / fadiga cíclica (500.000 ciclos, 2Hz, 5kg) não têm influência na microinfiltração marginal e 4) O armazenamento/fadiga cíclica não influenciam a integridade marginal das coroas. Grupos controle foram constituídos em todos os experimentos. Resultados: 1) Nenhuma diferença estatisticamente significante foi detectada entre as duas técnicas testadas para analisar a microinfiltração dentro de cada conjunto cimento/adesivo (p>0...

Crescimento de trinca subcrítico em cerâmicas odontológicas: efeito do material (microestrutura) e do método de ensaio; Growth of crack subcrítico in dental ceramics: effect of the material (Microstructure) and the test method

Gonzaga, Carla Castiglia
Fonte: Biblioteca Digitais de Teses e Dissertações da USP Publicador: Biblioteca Digitais de Teses e Dissertações da USP
Tipo: Tese de Doutorado Formato: application/pdf
Publicado em 17/08/2007 PT
Relevância na Pesquisa
46.29%
O objetivo deste trabalho foi realizar a caracterização microestrutural e das propriedades mecânicas de diferentes cerâmicas odontológicas para entender sua influência nos parâmetros de crescimento de trinca subcrítico (SCG), n (coeficiente de susceptibilidade ao SCG) e ?f0 (parâmetro escalar), determinados por diferentes métodos. Cinco cerâmicas foram avaliadas: porcelanas VM7 (Vita) e D (d.Sign, Ivoclar), vitrocerâmicas E1 (IPS Empress, Ivoclar) e E2 (IPS Empress 2, Ivoclar) e compósito IC (In-Ceram Alumina, Vita). Espécimes em forma de disco (12 mm x 1 mm) foram confeccionados segundo as recomendações dos fabricantes. A caracterização microestrutural dos materiais foi realizada. A tenacidade à fratura (KIc) foi determinada pelo método da fratura por indentação (IF) e indentation strength. Os parâmetros de SCG foram determinados por fadiga dinâmica (com diferentes taxas de tensão constante), fadiga estática (com diferentes níveis de tensão constante) e fadiga por IF. Os resultados mostraram que todas as cerâmicas constituíram-se de fase vítrea e cristalina, com exceção da VM7, composta somente por fase amorfa. D e E1 apresentaram partículas de leucita, em frações volumétricas iguais a 0,16 e 0...

Influência do tipo de sistema de infra-estrutura na adaptação e microinfiltração de coroas totais cerâmicas; Influence of the type of framework system in the adaptation and microleakage of all-ceramic crowns

Cavalcanti, Maria Tereza Moura de Oliveira
Fonte: Biblioteca Digitais de Teses e Dissertações da USP Publicador: Biblioteca Digitais de Teses e Dissertações da USP
Tipo: Tese de Doutorado Formato: application/pdf
Publicado em 04/04/2008 PT
Relevância na Pesquisa
66.61%
Os objetivos deste trabalho foram: a quantificação da microinfiltração e desadaptação antes e após cimentação de coroas totais cerâmicas, com quatro tipos de sistemas de infra-estrutura e a correlação entre desadaptação e microinfiltração. Após aprovação pelo Comitê de Ética da FOUSP, 40 terceiros molares humanos receberam coroais totais cerâmicas, sendo: 2 cerâmicas infiltradas por vidro (In-Ceram alumina Slip-Cast (S) e o bIoco In-Ceram Alumina CA-12 (CA)) e 2 cerâmicas de alumina policristalina (Procera/Nobel Biocare (P) e o bloco In-Ceram Al-20, CEREC In-Lab (CE)), (n=10). O espaço entre coroa e dente foi medido antes e depois da cimentação das coroas. Foram submetidos à ciclagem mecânica (100.000 ciclos, 8 Kgf, 4 Hz), térmica (700 ciclos, 5/55ºC por minuto), submersos em azul de metileno 0,5% por 4 horas e seccionados nos sentidos mésio/distal e vestíbulo/lingual. As imagens foram obtidas em estereomicroscópio (20X) e os dados de desadaptação foram submetidos à ANOVA (e Tukey). Os escores da microinfiltração foram submetidos à análise da concordância dos avaliadores e Kruskal-Wallis. Não houve diferenças significantes entre os sistemas cerâmicos (S= 38, P= 49, CA= 48 e CE= 39?m). O fator "região" da linha de cimentação apresentou diferenças estatísticas. A desadaptação foi maior na parede pulpar (60 ?m)...

Síntese e processamento de compósitos  á base de alumina e zircônia com infiltração de fase vítrea para aplicações  odontológicas; SYNTHESIS AND CERAMIC PROCESSING OF ALUMINA AND ZIRCONIA BASED COMPOSITES INFILTRATED WITH GLASS PHASE FOR DENTAL APPLICATIONS

Duarte, Daniel Gomes
Fonte: Biblioteca Digitais de Teses e Dissertações da USP Publicador: Biblioteca Digitais de Teses e Dissertações da USP
Tipo: Dissertação de Mestrado Formato: application/pdf
Publicado em 22/05/2009 PT
Relevância na Pesquisa
46.41%
O interesse pelo emprego de materiais cerâmicos na odontologia surgiu, inicialmente, devido ao excelente resultado estético proporcionado pela similaridade aos dentes naturais. Entretanto, a fragilidade, inerente das cerâmicas tradicionais, era uma limitação que impossibilitava a utilização em condições em que o material fosse submetido à solicitação mecânica. Com o desenvolvimento de materiais à base de alumina e zircônia, os quais conciliam aspecto estético, biocompatibilidade e bom desempenho mecânico, o emprego de cerâmicas na fabricação de restaurações dentais começou a ser considerado. A incorporação de fase vítrea de reforço nestas cerâmicas tem como finalidade minimizar as taxas de retração e melhorar a adesão ao agente cimentante resinoso, necessário para união da infraestrutura cerâmica à estrutura dental remanescente. Comercialmente, esses materiais são conhecidos como sistemas In-Ceram®. Considerando-se que o aprimoramento dos métodos de síntese e de técnicas de processamento de pós cerâmicos é um dos fatores fundamentais para o bom desempenho desses materiais, o presente trabalho teve como objetivo o estudo de obtenção de cerâmicas à base de alumina e/ou zircônia estabilizada com 3 mol% de ítria com infiltração de fase vítrea de aluminoborossilicato de lantânio...

Flexural Strength of Glass-Infiltrated Zirconia/Alumina-Based Ceramics and Feldspathic Veneering Porcelains

Bottino, Marco Antonio; Salazar-Marocho, Susana M.; Leite, Fabiola P. P.; Vasquez, Vanessa C.; Valandro, Luiz Felipe
Fonte: Wiley-Blackwell Publicador: Wiley-Blackwell
Tipo: Artigo de Revista Científica Formato: 417-420
ENG
Relevância na Pesquisa
56.5%
Purpose: To compare the flexural strength of two glass-infiltrated high-strength ceramics and two veneering glass-ceramics.Materials and Methods: Four ceramic materials were tested: two glass-infiltrated high-strength ceramics used as framework in metal-free restorations [In-Ceram Zirconia IZ (Gr1) and In-Ceram Alumina IA (Gr2)], and two glass-ceramics used as veneering material in metal-free restorations [Vita VM7 (Gr3) and Vitadur-alpha (Gr4)]. Bar specimens (25 x 5 x 2 mm(3)) made from core ceramics, alumina, and zirconia/alumina composites were prepared and applied to a silicone mold, which rested on a base from a gypsum die material. The IZ and IA specimens were partially sintered in an In-Ceram furnace according to the firing cycle of each material, and then were infiltrated with a low-viscosity glass to yield bar specimens of high density and strength. The Vita VM7 and Vitadur-alpha specimens were made from veneering materials, by vibration of slurry porcelain powder and condensation into a two-part brass Teflon matrix (25 x 5 x 2 mm(3)). Excess water was removed with absorbent paper. The veneering ceramic specimens were then removed from the matrix and were fired as recommended by the manufacturer. Another ceramic application and sintering were performed to compensate the contraction of the feldspar ceramic. The bar specimens were then tested in a three-point bending test.Results: The core materials (Gr1: 436.1 +/- 54.8; Gr2: 419.4 +/- 83.8) presented significantly higher flexural strength (MPa) than the veneer ceramics (Gr3: 63.5 +/- 9.9; Gr4: 57.8 +/- 12.7).Conclusion: In-Ceram Alumina and Zirconia were similar statistically and more resistant than VM7 and Vitadur-alpha.

Fatigue resistance of the bond of a glass-infiltrated alumina ceramic to human dentin

Baldissara, Paolo; Valandro, Luiz Felipe; Monaco, Carlo; Ferrari, Marco; Bottino, Marco Antonio; Scotti, Roberto
Fonte: Universidade Estadual Paulista Publicador: Universidade Estadual Paulista
Tipo: Artigo de Revista Científica Formato: 97-104
ENG
Relevância na Pesquisa
66.42%
Purpose: To evaluate the fatigue resistance of the bond between dentin and glass-infiltrated alumina ceramic, using different luting protocols. Materials and Methods: The null hypothesis is that the fatigue resistance varies with the luting strategy. Forty blocks of In-Ceram Alumina were prepared, and one surface of each block was abraded with 110-μm aluminum oxide particles. Then, the blocks were luted to flat dentin surfaces of 40 human third molars, using 4 different luting strategies (luting system [LS]/ceramic surface conditioning [CSC]) (n=10): (G1) [LS] RelyX-Unicem/[CSC] airborne abrasion with 110-μm Al2O3 particles; (G2) [LS] One-Step + Duo-Link (bis-GMA-based resin)/[CSC] etching with 4% hydrofluoric acid + silane agent; (G3) [LS] ED-Primer + Panavia F (MDP-based resin)/[CSC] Al2O 3; (G4) [LS] Scotchbond1+RelyX-ARC (bis-GMA-based resin)/[CSC] chairside tribochemical silica coating (air abrasion with 30-μm SiO x particles + silane). After 24 h of water storage at 37°C, the specimens were subjected to 106 fatigue cycles in shear with a sinusoidal load (0 to 21 N, 8 Hz frequency, 37°C water). A fatigue survivor score was given, considering the number of the fatigue cycles until fracture. The failure modes of failed specimens were observed in a SEM. Results: G3 (score = 5.9...

Microtensile bond strength of a resin cement to silica-coated and silanized in-ceram zirconia before and after aging

Valandro, Luiz Felipe; Özcan, Mutlu; Amaral, Regina; Leite, Fabiola Pessoa Pereira; Bottino, Marco Antonio
Fonte: Universidade Estadual Paulista Publicador: Universidade Estadual Paulista
Tipo: Conferência ou Objeto de Conferência Formato: 70-72
ENG
Relevância na Pesquisa
66.18%
Purpose: This study compared the microtensile bond strength of resin-based cement (Panavia F) to silica-coated, silanized, glass-infiltrated high-alumina zirconia (In-Ceram Zirconia) ceramic in dry conditions and after various aging regimens. Materials and Methods: The specimens were placed in 1 of 4 groups: group 1: dry conditions (immediate testing without aging); group 2: water storage at 37°C for 150 days; group 3: 150 days of water storage followed by thermocycling (× 12,000, 5°C to 55°C); group 4: water storage for 300 days; group 5: water storage for 300 days followed by thermocycling. Results: Group 1 showed a significantly higher microtensile bond strength value (26.2 ± 1 MPa) than the other aging regimens (6.5 ± 1, 6.2 ± 2, 4.5 ± 1, 4.3 ± 1 MPa for groups 2, 3, 4, and 5, respectively) (P < .01). Conclusion: Satisfactory results were seen in dry conditions, but water storage and thermocycling resulted in significantly weaker bonds between the resin cement and the zirconia.

Functional and esthetic rehabilitation with In-Ceram alumina and zirconia system: A multidisciplinary approach

Zavanelli, Adriana Cristina; Mazaro, José Vitor Quinelli; Mestrener, Sandra Rahal; Zavanelli, Recardo Alexandre
Fonte: Universidade Estadual Paulista Publicador: Universidade Estadual Paulista
Tipo: Artigo de Revista Científica Formato: 68-72
ENG
Relevância na Pesquisa
86.49%
The development of all-ceramic systems following metalceramics restorations allowed simulation of natural dentition due to favorable esthetics and resistance. In-Ceram is an alternative when esthetics is primordial as well as resistance required in rehabilitation. However, an ideal smile is associated to not only shape, color, texture and translucency but also harmony with gingival tissue. So, the aim of this study is to report a clinical case based on periodontal and fixed partial dentures principles to perform periodontal plastic surgery followed by esthetic rehabilitation. A female patient, 40-year-old, presented complaint about dental esthetics. After clinical and radiographic exams, metal-ceramics crowns (teeth 11, 12, 13, 21, 22 and 23) were considered unsatisfactory due to marginal leakage, color change in gingival tissue associated to metallic margin, and gummy smile. So, a crown lengthening surgery of anterior teeth was performed followed by rehabilitation of superior teeth with In-Ceram single crowns. Clinical significance: The interaction between periodontics and fixed prosthodontic area is the key of an adequated treatment planning which involves gingival smile to provide function and an esthetic condition in association with an esthetic...

Shear bond strength of resin cement bonded to alumina ceramic after treatment by aluminum oxide sandblasting or silica coating

Passos, Sheila Pestana; Valandro, Luiz Felipe; Bottino, Marco Antonio; Santos, Maria Jacinta Moraes Coelho; Santos Jr., Gildo Coelho
Fonte: Universidade Estadual Paulista Publicador: Universidade Estadual Paulista
Tipo: Artigo de Revista Científica Formato: 561-565
ENG
Relevância na Pesquisa
76.53%
Purpose: To evaluate the shear bond strength and bond durability between a dual-cured resin cement (RC) and a high alumina ceramic (In-Ceram Alumina), subjected to two surface treatments. Materials and Methods: Forty disc-shaped specimens (sp) (4-mm diameter, 5-mm thick) were fabricated from In-Ceram Alumina and divided into two groups (n = 20) in accordance with surface treatment: (1) sandblasting by aluminum oxide particles (50 μm Al 2O 3) (SB) and (2) silica coating (30 μm SiO x) using the CoJet system (SC). After the 40 sp were bonded to the dual-cured RC, they were stored in distilled water at 37°C for 24 hours. After this period, the sp from each group were divided into two conditions of storage (n = 10): (a) 24 h-shear bond test 24 hours after cementation; (b) Aging-thermocycling (TC) (12,000 times, 5 to 55°C) and water storage (150 days). The shear test was performed in a universal test machine (1 mm/min). Results: ANOVA and Tukey (5%) tests noted no statistically significant difference in the bond strength values between the two surface treatments (p= 0.7897). The bond strengths (MPa) for both surface treatments reduced significantly after aging (SB-24: 8.2 ± 4.6; SB-Aging: 3.7 ± 2.5; SC-24: 8.6 ± 2.2; SC-Aging: 3.5 ± 3.1). Conclusion: Surface conditioning using airborne particle abrasion with either 50 μm alumina or 30 μm silica particles exhibited similar bond strength values and decreased after long-term TC and water storage for both methods. © 2011 by The American College of Prosthodontists.

Efeito da fadiga cíclica na resistência, crescimento subcrítico de trincas e tempo de vida de cerâmicas a base de alumina infiltradas por vidro

Salazar Marocho, Susana María
Fonte: Universidade Estadual Paulista (UNESP) Publicador: Universidade Estadual Paulista (UNESP)
Tipo: Dissertação de Mestrado Formato: 150 f. : il. anexo
POR
Relevância na Pesquisa
46.48%
Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES); Pós-graduação em Odontologia Restauradora - ICT; O objetivo foi avaliar (1) a influência da microestrutura e composição de cerâmicas a base de alumina e infiltrada por vidro (IA- In-Ceram Alumina, Vita) e com reforço de zircônia (IZ- In-Ceram Zircônia, Vita) no comportamento mecânico quanto à resistência a flexão e fadiga; e (2) o efeito das cargas cíclicas na resistência (σ), crescimento subcrítico de trincas (CST) e tempo de vida (TV) desses materiais cerâmicos. Noventa corpos-de-prova (CP) (1.2 x 4 x 20 mm3) de cada material foram fabricados de acordo com ISO 6872 e instruções do fabricante. Os CP de IA e IZ foram divididos em 6 grupos (n=15), submetidos a: 1) flexão em três pontos em saliva artificial a 37°C (IA3P e IZ3P); e 2) fadiga cíclica em ambiente seco e úmido (IAFS, IAFU, IZFS, IZFU). A resistência inicial (σc) e o número de ciclos nos quais cada CP fraturou foram obtidos a partir do ensaio de flexão (3P) e da fadiga cíclica, respectivamente; e avaliados pela análise estatística de Weibull. O CST foi calculado a partir da velocidade da trinca em função da intensidade máxima de estresse. Para estimar o TV foi utilizado o diagrama de Wöhler (DW). Os valores de σc (MPa) da IA variaram de 340 a 560...

Análise da influência de diferentes tratamentos superficiais de sistemas cerâmicos na resistência de união adesiva

Vasconcellos, Walison Arthuso
Fonte: Universidade Estadual Paulista (UNESP) Publicador: Universidade Estadual Paulista (UNESP)
Tipo: Tese de Doutorado Formato: 132 f. : il.
POR
Relevância na Pesquisa
46.55%
Pós-graduação em Ciências Odontológicas - FOAR; A cimentação é vital para o sucesso clínico de restaurações cerâmicas puras e é dependente de muitos fatores como a composição dos materiais cerâmicos, tratamento de superfície, e agente cimentante. O objetivo deste estudo foi investigar a influência de diferentes tratamentos superficiais (microjateamento, microjateamento + condicionamento com ácido fluorídrico e silicatização) de diferentes materiais cerâmicos (Duceram Plus - Degussa, IPS Empress 2 - Ivoclar Vivadent, In-Ceram Alumina - Vita) na resistência de união adesiva, usando o teste de microtração. Dezoito terceiros molares humanos superiores recém extraídos foram usados. Os dentes foram limpos e mantidos em solução salina com timol a 0.2% em temperatura ambiente. A superfície oclusal foi cortada perpendicular ao longo eixo do dente com disco diamantado em baixa rotação em máquina de corte. Os dentes foram aleatoriamente divididos em três grupos (n=6) da seguinte forma: Grupo I. Duceram Plus - Degussa; Grupo II. IPS Empress 2 - Ivoclar Vivadent; and Grupo III. In-Ceram Alumina - Vita. Moldagens foram feitas em todos os dentes com silicona de adição e obtidos troquéis em gesso tipo IV. Cada grupo foi dividido em três subgrupos (n=2)...

Estudo comparativo da adaptação entre copings metalicos e de alumina, no sistema In-Ceram, antes e apos cimentação; Comparative study of the adaptation between metallic copings and alumina, in system In-Ceram, before and after cementation

Ligia Luzia Buarque e Silva
Fonte: Biblioteca Digital da Unicamp Publicador: Biblioteca Digital da Unicamp
Tipo: Dissertação de Mestrado Formato: application/pdf
Publicado em 28/02/2007 PT
Relevância na Pesquisa
46.47%
Este estudo analisou comparativamente a adaptação marginal antes e após a cimentação de copings metálicos e de alumina, no sistema In-Ceram, em preparos sobre dentes bovinos, utilizando dois tipos de cimento. Sessenta incisivos bovinos foram fixados em resina acrílica ativada quimicamente e as porções coronárias foram preparadas para coroa total, utilizando pontas diamantadas tronco cônica no 4103 com paredes axiais com expulsividade de 8o e término cervical em ombro. Trinta coroas foram confeccionadas para cada tipo de coping. Após, os copings foram adaptados sobre os preparos com carga estática de 9 Kgf por 1 minuto e a discrepância marginal foi medida com microscópio de mensuração (STM). Em seguida, os copings foram removidos e 15 amostras de cada tipo de coping foram cimentados sobre os dentes com cimento de fosfato de zinco (SS White, Petrópolis, RJ. Brasil) e 15 com cimento resinoso (Rely X ARC 3M/ESPE Divisão Dental ? Brasil), aplicou-se uma carga estática de 9 Kgf por 7 minutos e novamente a discrepância marginal foi medida. Os resultados foram submetidos à Análise de Variância e ao Teste de Tukey (5%) e indicaram que os dois tipos de copings apresentaram desajuste cervical após a cimentação estatisticamente superior ao desajuste cervical antes da cimentação...

Estudo comparativo da adaptação marginal entre copings metalicos, In-Ceram alumina e e.max Press, antes e apos a cimentação; Comparative study of the adaptation between metallic copings, In-Cream alumina and e.max Press, before and after cementation

Ligia Luzia Buarque e Silva
Fonte: Biblioteca Digital da Unicamp Publicador: Biblioteca Digital da Unicamp
Tipo: Tese de Doutorado Formato: application/pdf
Publicado em 10/02/2010 PT
Relevância na Pesquisa
56.36%
Esse estudo avaliou a adaptação marginal entre copings metálicos, In-Ceram e e.max Press, antes e após cimentação em preparos sobre dentes bovinos, utilizando dois tipos de cimento resinosos. Noventa incisivos bovinos foram fixados em resina acrílica ativada quimicamente e as porções coronárias foram preparadas para coroa total, com expulsividade de 8o e término cervical em ombro. Trinta copings foram confeccionados para cada tipo de material, onde foram adaptados sobre os preparos com carga estática de 9 Kgf por 1 minuto e a discrepância marginal foi medida com microscópio de mensuração (STM). Em seguida, 15 amostras para cada tipo de coping foram cimentadas sobre os dentes com agente resinoso convencional, e mais 15 amostras para cada coping foram cimentadas com agente autoadesivo com uma carga estática de 9 Kgf por 7 minutos e novamente a discrepância marginal foi medida. Os resultados mostraram que antes da cimentação, houve diferenças significativas (p<0,05) no desajuste marginal entre os sistemas, sendo que o e.max Press apresentou maior desajuste. Após a cimentação os copings de metal e In-Ceram não apresentaram diferenças significativas (p>0,05) entre os cimentos. O sistema e.max Press apresentou um maior desajuste (p<0...

Influence of handling and heating cycle on the morphology and flexural strength of glass-infiltrated alumina bars

Da Silva,F.T.; Barbejat,A.; Filho,H.S.
Fonte: Rede Latino-Americana de Materiais Publicador: Rede Latino-Americana de Materiais
Tipo: Artigo de Revista Científica Formato: text/html
Publicado em 01/03/2008 EN
Relevância na Pesquisa
56.48%
The main goal of the present study was to evaluate the influence of plaster stability, handling and thermal cycling on the morphology and mechanical strength of glass infiltrated alumina bars. Two different slip casting/thermal processing routes were investigated. The highest flexural strength of alumina bars from In-Ceram® Alumina protocol in comparison to In-Ceram® Sprint protocol was mainly due to its low drying rate and less handling. After glass infiltration and mechanical surface treatments, In-Ceram®Sprint alumina bars presented a non-homogeneous distribution of alumina particles in the glass phase, which was the mais cause for its lower flexural strength. In both cases, it was observed a strong anisotropic growth of alumina particles after glass infiltration. Non-reproducible mechanical surface treatments is other factor that could deteriorate the mechanical strength of alumina bars.

Caracterização micrográfica de próteses dentais de alumina infiltrada com vidro de lantânio e sua correlação com a resistência à flexão por três pontos

Ogasawara,T.; Silva,P.T.G.; Silva,R.C.; Pinto,V.B.B.
Fonte: Rede Latino-Americana de Materiais Publicador: Rede Latino-Americana de Materiais
Tipo: Artigo de Revista Científica Formato: text/html
Publicado em 01/03/2008 PT
Relevância na Pesquisa
56.52%
Estudou-se a infiltração (em diferentes condições) do vidro de lantânio em alumina parcialmente sinterizada e a sua relação com a resistência à flexão. As barras de In-Ceram Alumina, fraturadas em flexão por 3 pontos, foram lixadas, polidas e caracterizadas por microscopias ótica e eletrônica de varredura (MEV). Foram usadas 10 barras para cada condição operacional. Resultados: (a) A MEV confirma que os núcleos de barras In-Ceram Alumina (sinterizados a 1120ºC durante 2h) infiltrados a 1100ºC durante 6h contém menos vidro de lantânio do que aqueles das barras infiltradas durante 6h a 1110ºC; (b) A micrografia ótica confirma que os núcleos de barras In-Ceram Alumina (sinterizada a 1120ºC durante 2h) infiltrada durante 6h (ou 2h) nas temperaturas de 1100ºC, 1100ºC, 1120ºC e 1130ºC não se diferem notavelmente; (c) A MEV mostra que a microestrutura interna de barras In-Ceram Alumina infiltradas com vidro de lantânio a 1120ºC e 1130ºC é complexa.

Estudo de sistemas vítreos para infiltração em alumina; Study of glass system to alumina infiltration

Queiroz, José Renato Cavalcanti de
Fonte: Universidade Federal do Rio Grande do Norte; BR; UFRN; Programa de Pós-Graduação em Ciência e Engenharia de Materiais; Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part Publicador: Universidade Federal do Rio Grande do Norte; BR; UFRN; Programa de Pós-Graduação em Ciência e Engenharia de Materiais; Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part
Tipo: Dissertação Formato: application/pdf
POR
Relevância na Pesquisa
56.52%
The system in-Ceram Alumina, produced by VITA, consists in a technique of prepare of a substructure of ceramics to dental crowns. First burning is made in the alumina decanted by slip casting process under a stone die that reproduces the tooth prepared to receive a crown. In a second burning, alumina is infiltrated by vitreous system, giving to this set a high mechanic resistance. In this work, it s made a study of the composition of a new infiltrating material more used nowadays, giving to alumina desirable mechanics proprieties to its using like substructure of support to ceramic s crown used in the market today. The addition of Lanthanum oxide (frit A) and calcium oxide (frit B) was made in attempt to increase the viscosity of LZSA and to reduce fusion temperature. The frits were put over samples of alumina and took to the tubular oven to 1400ºC under vacuum for two groups (groups 1 and 2). For another two groups (groups 3 and 4) it was made a second infiltration, following the same parameters of the first. A fifth group was utilized like group of control where the samples of pure alumina were not submitted to any infiltrating process. Glasses manifested efficient both in quality and results of analysis of mechanic resistance...

Estruturas cerâmicas a base de zircônia e alumina utilizadas na confecção de infra - estruturas para coroas e pontes fixas

Silva, Cláudia Anglélica Melo da
Fonte: Universidade Federal do Rio Grande do Norte; BR; UFRN; Programa de Pós-Graduação em Ciência e Engenharia de Materiais; Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part Publicador: Universidade Federal do Rio Grande do Norte; BR; UFRN; Programa de Pós-Graduação em Ciência e Engenharia de Materiais; Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part
Tipo: Dissertação Formato: application/pdf
POR
Relevância na Pesquisa
46.4%
The continuous advances in ceramic systems for crowns and bridges infrastructure getting researchers and manufacturers looking for a material that has good mechanical properties and aesthetic. The purpose of this study was to verify in which composition and sintering temperature the ceramic system for infrastructure composed of alumina and zirconia would have the best mechanical properties. With this objective we made in UFRN laboratories 45 test bodies in the form of rectangular bars with the following dimensions: 30mm x 8mm x 3mm, where we separated by the sintering temperature: 1200°C, 1300ºC and 1400ºC, and by comp osition: 33% Zirconia + 67% Alumina; 50% Zirconia + 50% Alumina and 25% Zirconia + 75% Alumina, these test bodies were not infiltrated with glass. Also, were made nine test bodies by a technical from a laboratory with a commercial ceramic system: in the Ceram Zircônia (Vita - Zahnfabrik) with the following dimensions: 20mm x 10mm x 0.5mm, these test bodies following all recommendations of the manufacturer and were infiltrated with glass. Were realized optical and electronic microscopy analyses, hardness testing, resistance to bending in three points, porosity and bulk density. After analysis of the results we verified that with the increasing of sintering temperature...

Porcelain monolayers and porcelain/alumina bilayers reinforced by Al2O3/GdAlO3 fibers

Sgura, Ricardo; Medeiros, Igor Studart; Cesar, Paulo Francisco; Campos, Adeliani Almeida; Hernandes, Antonio Carlos
Fonte: ELSEVIER SCIENCE BV; AMSTERDAM Publicador: ELSEVIER SCIENCE BV; AMSTERDAM
Tipo: Artigo de Revista Científica
ENG
Relevância na Pesquisa
46.34%
Aim. This work tested the effect of the addition of Al2O3/GdAlO3 longitudinal fibers in different contents to veneering porcelain of two dental all ceramic systems. Methods: Fibers (0.5 mm diameter) obtained by the Laser Heated Pedestal Growth (LHPG) method were added to bar-shaped specimens made by veneer porcelain (monolayers) or both the veneer and the core ceramic (bilayers) of two all-ceramic systems: In-Ceram Alumina - glass infiltrated alumina composite (GIA) and In-Ceram 2000 AL Cubes - alumina polycrystal (AP) (VITA Zahnfabrik). The longitudinal fibers were added to veneering porcelain (VM7) in two different proportions: 10 or 17 vol%. The bars were divided into nine experimental conditions (n = 10) according to material used: VM7 porcelain monolayers, VM7/GIA, VM7/AP; and according to the amount of fibers within the porcelain layer: no fibers, 10 vol% or 17 vol%. After grinding and polishing the specimens were submitted to a three point bending test (crosshead speed = 0.5 mm/min) with porcelain positioned at tensile side. Data were analyzed by means of one-way ANOVA and a Tukey's test (alpha = 5%). Scanning electronic microscopy (SEM) was conducted for fractographic analysis. Results. Regarding the groups without fiber addition...

Efeito do tratamento de superfície de uma cerâmica aluminizada infiltrada de vidro sobre a resistência à microtração; Effect of surface treatment of a glass-infiltrated alumina ceramic on the microtensile bond strength

Michida, Silvia Masae de Araujo; Valandro, Luiz Felipe; Yoshiga, Silvia; Andreatta Filho, Osvaldo Daniel; Balducci, Ivan; Bottino, Marco Antonio
Fonte: Universidade de São Paulo. Faculdade de Odontologia de Bauru Publicador: Universidade de São Paulo. Faculdade de Odontologia de Bauru
Tipo: info:eu-repo/semantics/article; info:eu-repo/semantics/publishedVersion; ; Formato: application/pdf
Publicado em 01/12/2003 POR
Relevância na Pesquisa
56.32%
Este estudo avaliou a resistência à microtração entre um cimento resinoso e uma cerâmica submetida a três tratamentos de superfície. Foram confeccionados 12 blocos da cerâmica In-Ceram Alumina (VITA) e 12 blocos de resina composta (Clearfil APX, Kuraray) com dimensões de 6mm x 6mm x 5mm. A superfície da cerâmica foi polida com lixas d'água nº 600, 800 e 1200 sob refrigeração, e os blocos foram divididos em três grupos conforme o tratamento superficial: Grupo 1 - Jateamento com óxido de alumínio 110mm; Grupo 2 - Sistema Rocatec (3M/ESPE): jateamento com óxido de alumínio 110mm (Rocatec-pre powder) e com sílica (Rocatec-plus powder) + silano (Rocatec-Sil); Grupo 3 - Sistema CoJet (3M/ESPE): jateamento com partículas de sílica 30mm + ESPE-Sil. Os blocos cerâmicos foram cimentados aos de resina composta com o cimento resinoso Panavia F (Kuraray Co) conforme as instruções do fabricante, sob carga de 750g por 10min. As amostras foram armazenadas (água destilada/37ºC/7 dias) e seccionadas em dois eixos, x e y, com disco diamantado sob refrigeração em uma máquina de corte a fim de obter corpos-de-prova (CP) com 0,6±0,1mm² de área adesiva (n=36). Os CP foram fixados em dispositivo adaptado para o teste de microtração e tracionados (velocidade: 0...