PUSHING THE BOUNDARIES OF CONCENTRATED DISPERSIONS, High Solids Content Bimodal Latex for Paper Coating Applications

Pacheco de Moraes, Raul
Fonte: Quens University Publicador: Quens University
Tipo: Tese de Doutorado
EN; EN
Relevância na Pesquisa
36.71%
New processes for the production of polymeric dispersions with high solids content and low viscosity were developed, investigated and characterized. The specifications required for the desired application of paper coating, which constitutes one of the major innovative aspects of this thesis, requires in average particle sizes smaller than 200 nm. This particle size is significantly smaller than obtained in previous work in this area. The main objective of this project was to increase the solids content of existing products from ~50 to ~60 wt% while keeping the viscosity at low levels (< 1200 mPa•s at 20 s-1). In order to produce high solids content latexes with low viscosity, bimodal particle size distributions were resorted to. To obtain highest packing fraction, the small particle size population should be about 7 times smaller than the large particles, bringing the size of the small particles to less than 30 nm. Modified (micro)emulsion processes were developed in order to produce small particle size latex with reduced surfactant concentration and increased solids content. The large particle population was developed using a semi-batch emulsion polymerization process, simulating a product that is commercially available (~52 wt% solids content and viscosity of ~500 mPa•s at 20 s-1). To increase the solids content of this product up to 60 wt%...